Product Properties,
1. Low resin demand
2. Good abrasion resistance
3. Good processing characteristics
4. Rapid and complete wet out
5. High composite machanical properties
6. Multi-compatible Sizing
Package,
The roving to be packed on 20 pallets for a 20' container. The detailed package is listed as follows,
4 X 4 rolls/layer, 4 layer/pallet, 10 pallets
4 X 4 rolls/layer, 3 layer/pallet, 10 pallets.
Each layer is seperated with paperboard.Each pallet is supported by very strong papercoil at the four corners of pallet, then packed in big carton, wrapped in a polythene stretched film. The roving on pallet after package is visible.
Storage,
Unless otherwise specified, fiberglass products should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15℃-35℃ and 35%-65% respecitively. To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high. When the pallets are stacked in 2 or 3 layers, care should be taken to correctly and smoothly move the top pallet.
1. Low resin demand
2. Good abrasion resistance
3. Good processing characteristics
4. Rapid and complete wet out
5. High composite machanical properties
6. Multi-compatible Sizing
Package,
The roving to be packed on 20 pallets for a 20' container. The detailed package is listed as follows,
4 X 4 rolls/layer, 4 layer/pallet, 10 pallets
4 X 4 rolls/layer, 3 layer/pallet, 10 pallets.
Each layer is seperated with paperboard.Each pallet is supported by very strong papercoil at the four corners of pallet, then packed in big carton, wrapped in a polythene stretched film. The roving on pallet after package is visible.
Storage,
Unless otherwise specified, fiberglass products should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15℃-35℃ and 35%-65% respecitively. To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high. When the pallets are stacked in 2 or 3 layers, care should be taken to correctly and smoothly move the top pallet.
Direct roving for filament winding is typcailly used to produce FRP pipes of various diameters, storage tanks and rods which are widely used in transportation, aviation and space, military and electrical industries.
Linear density（％）ISO 1889: ±5
Moisture content（％）ISO 3344: ≤0.10
Size content（％）ISO 1887: 0.55±0.15
Breaking strength（N/tex）ISO 3341: ≥0.40
Net weight（kg）: ≥13.0
Moisture content（％）ISO 3344: ≤0.10
Size content（％）ISO 1887: 0.55±0.15
Breaking strength（N/tex）ISO 3341: ≥0.40
Net weight（kg）: ≥13.0