Product Properties,
1. Low static
2. Good choppability
3. Good dispersion and uniform distribution
4. Moderate wet-out and good compatibility
Package,
The roving to be packed on 20 pallets for a 20' container. The detailed package is listed as follows,
4 X 4 rolls/layer, 4 layer/pallet, 10 pallets
4 X 4 rolls/layer, 3 layer/pallet, 10 pallets.
Each layer is seperated with paperboard.Each pallet is supported by very strong papercoil at the four corners of pallet, then packed in big carton, wrapped in a polythene stretched film. The roving on pallet after package is visible.
Storage,
Unless otherwise specified, fiberglass products should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15℃-35℃ and 35%-65% respecitively. To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high. When the pallets are stacked in 2 or 3 layers, care should be taken to correctly and smoothly move the top pallet.
1. Low static
2. Good choppability
3. Good dispersion and uniform distribution
4. Moderate wet-out and good compatibility
Package,
The roving to be packed on 20 pallets for a 20' container. The detailed package is listed as follows,
4 X 4 rolls/layer, 4 layer/pallet, 10 pallets
4 X 4 rolls/layer, 3 layer/pallet, 10 pallets.
Each layer is seperated with paperboard.Each pallet is supported by very strong papercoil at the four corners of pallet, then packed in big carton, wrapped in a polythene stretched film. The roving on pallet after package is visible.
Storage,
Unless otherwise specified, fiberglass products should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15℃-35℃ and 35%-65% respecitively. To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high. When the pallets are stacked in 2 or 3 layers, care should be taken to correctly and smoothly move the top pallet.
E-glass fiber chop roving is mainly designed as a reinforcement for GRP pipes. It is treated with a special silane-based siz and compatible with UP and vinyl ester resins. The product offers strong resin adsorbability and the end products have strong water resistance and excellent chemical resistance. The roving is typically used to make GRP pipes.
Linear density（％）ISO 1889: ±6
Moisture content（％）ISO 3344: ≤0.15
Size content（％）ISO 1887: 1.10±0.15
Stiffness (MM)ISO 3375: 115 ± 20
Net weight（kg）: 17.0±0.5
Moisture content（％）ISO 3344: ≤0.15
Size content（％）ISO 1887: 1.10±0.15
Stiffness (MM)ISO 3375: 115 ± 20
Net weight（kg）: 17.0±0.5